• Ciao Guest - You’ve landed at the ultimate Guzzi site. NEW FORUM REGISTRATIONS REQUIRE EMAIL ACTIVATION - CHECK YOUR SPAM FOLDER - Use the CONTACT above if you need help. New to the forum? For all new members, we require ONE post in the Introductions section at the bottom, in order to post in most of the other sections. ALWAYS TRY A SEARCH BEFORE STARTING A NEW TOPIC - Most questions you may have, have likely been already answered. DON'T BE A DRIVE-BY POSTER: As a common courtesy, check back in and reply within 24 hours, or your post will be deleted. Note there's decades of heavily experienced Guzzi professionals on this site, all whom happily give endless amounts of their VALUABLE time for free; BE COURTEOUS AND RESPECTFUL!
  • There is ZERO tolerance on personal attacks and ANY HYPERLINKS to PRODUCT(S) or other competing website(s), including personal pages, social media or other Forums. This ALSO INCLUDES ECU DIAGnostic software, questions and mapping. We work very hard to offer commercially supported products and to keep info relevant here. First offense is a note, second is a warning, third time will get you banned from the site. We don't have the time to chase repeat (and ignorant) offenders. This is NOT a social media platform; It's an ad-free, privately funded website, in small help with user donations. Be sure to see the GTM STORE link above; ALL product purchases help support the site, or you can upgrade your Forum profile or DONATE via the link above.
  • Be sure to see the GTM STORE link also above for our 700+ product inventory, including OEM parts and many of our 100% Made-in-SoCal-USA GTM products and engine kits. In SoCal? Click the SERVICE tab above for the best in service, tires, tuning and installation of our products or custom work, and don't miss our GT MotoCycles® (not) art on the BUILDS tab above. WE'RE HERE ONLINE ONLY - NO PHONE CALLS MADE OR RECEIVED - DO NOT EMAIL AND ASK QUESTIONS OR ASK TO CALL YOU.
  • Like the new V100, GuzziTech is full throttle into the future! We're now running on an all-new server and we've updated our Forum software. The visual differences are obvious, but hopefully you'll notice the super-fast speed. If you notice any glitches or have any issues, please post on the Site Support section at the bottom. If you haven't yet, please upgrade your account which is covered in the Site Support section or via the DONATE tab above, which gives you full site access including the DOWNLOADS section. We really appreciate every $ and your support to keep this site ad-free. Create an account, sign in, upgrade your account, and enjoy. See you on the road in 2024.

Battery Terminal Corrosion: Explanation, Cleaning & Prevention

GTM®

Administrator
Staff member
GT di Razza Pura
Joined
Jul 1, 2009
Messages
15,055
Location
Malibu
This has come up a great deal recently regarding newer bikes and battery terminal connections... so a FAQ stolen from this source.

Occasionally terminals or posts of lead acid batteries corrode due to which connection between batteries and appliance cuts off completely or weakens. In vehicles, corrosion restricts ignition of engines because enough current is not drawn from batteries. What causes this corrosion, what compounds are formed on terminals, and how to prevent this corrosion from happening again, complete details are given below. Equations of chemical reactions are also mentioned to help understand the process of corrosion.

Cause And Compounds Formation:
In case of sealed lead acid battery (also known as SLA battery or dry battery), corrosion happens when electrolyte makes its way out to battery terminals through any leaks or joints. In case of flooded lead acid batteries (wet batteries), electrolyte can jump out while carelessly pouring water into cells. Also, fumes of sulphuric acid which is a part of electrolyte and actually responsible for corrosion keeps arising out of vents of flooded lead acid batteries when battery is charging or hot. Overcharging heats up the battery and heat increases the volume of electrolyte filled inside it. This electrolyte can leak out of vents of overcharged flooded lead acid battery if it is topped up with too much water and also SLA batteries through loose joints.

Sometimes, it also happens that copper clamps or ringed copper terminals which are used to connect battery with wires corrode. Copper itself is not reactive even if dilute sulphuric acid is poured on it. But when electricity passes, it reacts with sulphuric acid and produce copper sulphate ( CuSO4 ) along with water and sulphur dioxide gas. The equation of this chemical reaction is following:


The white substance which you see around battery terminals is either lead sulphate made from the reaction explained one paragraph above or anhydrous copper sulphate made from the reaction explained in above paragraph. Anhydrous copper sulphate changes to blue colour when water is added to it. The bluish substance which you see around corroded copper terminals or copper clamps is hydrated copper sulphate.

Cleaning Corroded Battery Terminals:
To clean lead sulphate or copper sulphate from terminals, first disconnect terminals from battery. Make sure, you are wearing gloves as these chemicals can affect the skin. Now, wash terminals with clean water. If rust washes away, then no more hassles. Otherwise, wash them with the solution of any of these bases caustic soda, washing soda or baking soda made by dissolving base into water. Simply dipping battery terminals or clamps for few minutes into solutions of these bases also works. After cleaning with base solution, wash terminals again with clean water to clear away the remnants of base.

It is advised not to pour the solution of any of these bases over battery posts to clean them as it might gain access to battery interiors through vents, joints or leaks. If entered, it can badly affect the performance of battery. Instead, use a cloth dipped in base solution to clean them or use a brush to rub the rust off. Take extra precautions while cleaning hydrated copper sulphate which is bluish in colour because it is poisonous.

Prepared solutions are also available in markets to clean the corrosion. You can also use them.

Prevention from Corrosion:
1- Corrosion can occur in dry environment but it is boosted by moisture and salts present in water. Therefore, keep the batteries away from moisture and damp places.

2- Do not wash interior of car engine with water. Water increases speed of rusting metallic parts of engine which are not covered with paint and also joints of power cables and battery terminals.

3- Always keep the battery top dry and free from dust and other pollutants. After pouring water into flooded lead acid battery, never forget to dry the surface of battery. Close the caps of individual cells tightly.

4- Apply Petroleum jelly or grease to battery terminals to protect them from corrosion.

5- Use clamps and battery terminals made from good quality copper which are also alloy plated. Layer of alloy prevents terminals from corroding.
 
Thanks for the info. and great timing!
My Stelvio gave me a ECU disconnected message last week while i was riding with some buddies off road.
After i pulled off the seat i noticed my terminals had corrosion (all those water crossing i did a while ago probably didn't help). Took em apart, scraped them with a knife (trail fix) and it worked.
I'm going to give them a proper cleaning tonite and will put petroleum jelly as you stated.
 